アブレージョンパターンの生成とゴムの磨耗
https://doi.org/10.24517/00011675
https://doi.org/10.24517/000116750f70d95a-c4ad-4035-9c5e-bbf65dc70142
| 名前 / ファイル | ライセンス | アクション |
|---|---|---|
AN00044309-1987-UCHUYAMA-Y-111.pdf (983.8 kB)
|
.png)
|
| Item type | 紀要論文 / Departmental Bulletin Paper(1) | |||||
|---|---|---|---|---|---|---|
| 公開日 | 2017-10-03 | |||||
| タイトル | ||||||
| タイトル | アブレージョンパターンの生成とゴムの磨耗 | |||||
| タイトル | ||||||
| タイトル | The Formation of Abrasion Patterns and the Wear of Rubber | |||||
| 言語 | en | |||||
| 言語 | ||||||
| 言語 | jpn | |||||
| 資源タイプ | ||||||
| 資源タイプ識別子 | http://purl.org/coar/resource_type/c_6501 | |||||
| 資源タイプ | departmental bulletin paper | |||||
| ID登録 | ||||||
| ID登録 | 10.24517/00011675 | |||||
| ID登録タイプ | JaLC | |||||
| 著者 |
内山, 吉隆
× 内山, 吉隆× 沢井, 宗美 |
|||||
| 著者別表示 |
Uchiyama, Yoshitaka
× Uchiyama, Yoshitaka× Sawai, Muneyoshi |
|||||
| 書誌情報 |
金沢大学工学部紀要 = Memoirs of the Faculty of Technology, Kanazawa University 巻 20, 号 2, p. 111-121, 発行日 1987-03-01 |
|||||
| ISSN | ||||||
| 収録物識別子タイプ | ISSN | |||||
| 収録物識別子 | 0022-832X | |||||
| NCID | ||||||
| 収録物識別子タイプ | NCID | |||||
| 収録物識別子 | AN00044309 | |||||
| 出版者 | ||||||
| 出版者 | 金沢大学工学部 = the Faculty of Technology, Kanazawa University | |||||
| 抄録 | ||||||
| 内容記述タイプ | Abstract | |||||
| 内容記述 | Wheels of an unfilled isoprene rubber(unfilled IR) and a carbon-black-filled natural rubber(filled NR) were rubbed against a cylinder or a razor blade, and the formation mechanisms of abrasion patterns and the wear mechanisms of rubber were examined. When the abrasion patterns were formed on the rubber surfaces, small particles by roll-formation were observed in the early stage of wear. They grew up to relatively large in size and adhered to the rubber surface. Then cracks were formed just beneath the front portion of the adhered particles and grew large to form a series of the abrasion patterns having saw teeth. During motion of the slider the teeth are bent backwards, thus exposing their underside to the action of the slider. So the wear of the underside portions and tearing of their ridges seem to be important as well as the crack growth. Pattern abrasion tends to occur at high loads and on rough rubber surfaces. The other hand oily wear debris was produced under low loads and on smooth rubber surfaces. Pattern abrasion for the unfilled IR was observed at higher loads than that for the filled NR. It may represent the easy oxidation of the unfilled IR compared to the filled NR. |
|||||