 note = {本研究では，既存のPVDコーティング装置に“磁界ステアリング型アークプラズマ蒸発源”を増設して多層・複合膜の生成が可能な対向電極型アーク放電プロセス成膜装置を構築し，高温雰囲気で潤滑性と耐摩耗性に優れるVN/AlCrN-複合膜(8層および116層)の創成を行った．構築した多層膜はVN 膜と同様に高温領域で摩擦係数が減少するが，500℃まで常温硬度を維持しており，切削工具に適用できるレベルの潤滑性と耐熱性をもつことがわかった．その後，コーティングエンドミルによるプリハードン鋼の乾式切削を行った結果，高切削速度条件においても逃げ面摩耗幅が小さく，切削温度も低いことが明らかになった．, The multilayer coatings with lubricious VN and heat resistant AlCrN are developed. According to the nanoindentation hardness, critical scratch load, and friction coefficient, the multilayer VN/AlCrN-coated films have mechanical and tribological properties to comparable to those of the TiN, AlCrN, and VN films. Owing to the formation of Magneli-phase oxides, the friction coefficient decreased as the temperature increased above approximately 500deg.
The cutting forces of the VN-rich VN/AlCrN-coated tools were lower than those of TiN and AlCrN-rich tools, which were mainly caused by the tribological effect of the lubricious VN film. Meanwhile, the flank wear width of the multilayer VN/AlCrN-coated tools were relatively small due to the higher harness of the VN film. In addition, the cutting temperature of the VN/AlCrN-coated tools were considerably lower than that of the VN-coated tool, indicating a synergetic effect for wear resistant AlCrN and self-lubricating VN coating materials., 研究課題/領域番号:18H01349, 研究期間(年度):2018-04-01 - 2021-03-31, 出典：「窒化バナジウムを含有する高温潤滑複合コーティング膜の開発とその難削材加工への適用」研究成果報告書　課題番号18H01349
（KAKEN：科学研究費助成事業データベース（国立情報学研究所）） 
（https://kaken.nii.ac.jp/report/KAKENHI-PROJECT-18H01349/18H01349seika/）を加工して作成},
 title = {窒化バナジウムを含有する高温潤滑複合コーティング膜の開発とその難削材加工への適用},
 year = {2021}
}