 note = {We have developed a chemical modification process for the surface of nanodiamond particles using supercritical CO2. Using surface chemical modifiers (stearic acid and p-aminobenzoic acid), the relationship between the amount of modification on the nanodiamond surface and operating conditions and the effect of the phase state of the surface modifier were examined. In addition, the chemical bonding on the surface of the modified nanoparticles was clarified by by infrared absorption spectra, TG, and TEM, etc. Also the dispersibility of the modified nanodiamond in organic solvent was clarified by the average particle size distribution. Furthermore, since the concentration of the surface modifier greatly affects the chemical reaction mechanism, we developed a experimental apparatus for the solubility of the surface modifier in supercritical CO2 and obserbed the behavior of the solubility. We also developed thermodynamic analysis and calculation methods by various state equations., 超臨界CO2を用いたナノダイヤモンド粒子表面化学修飾プロセス開発を行った。表面化学修飾剤（ステアリン酸及びパラアミノ安息香酸）を用いて，ナノダイヤモンド表面での修飾量と操作条件の関係及び表面改質剤の相状態による影響を明らかにした。また，修飾ナノ粒子表面での化学結合状態について，赤外吸収スペクトル，熱重量分析，透過型電子顕微鏡等により，有機溶媒中での分散性平均粒度分布測定により明らかにした。さらに表面改質剤濃度が化学反応機構に大きく影響を与えるため，超臨界CO2中での表面改質剤の溶解度を，測定装置を開発し，溶解度の挙動を明らかにした。また，各種状態式による熱力学的解析と計算手法の開発を行った。, 研究課題/領域番号:19H02495, 研究期間(年度):2019-04-01 – 2022-03-31, 出典：研究課題「超臨界CO2を用いたナノダイヤモンド表面修飾における化工物性と機能性設計への展開」課題番号19H02495
（KAKEN：科学研究費助成事業データベース（国立情報学研究所）） 
（https://kaken.nii.ac.jp/ja/report/KAKENHI-PROJECT-19H02495/19H02495seika/）を加工して作成, 金沢大学理工研究域機械工学系},
 title = {超臨界CO2を用いたナノダイヤモンド表面修飾における化工物性と機能性設計への展開},
 year = {2022}
}