微小欠陥を含む部材の応力腐食割れおよび破壊靭性に関する研究
https://doi.org/10.24517/00067922
https://doi.org/10.24517/00067922e39a3f99-30f6-4784-9e64-51a6aae3bae5
| 名前 / ファイル | ライセンス | アクション |
|---|---|---|
ED-PR-HIROSE-Y-kaken 1989-2p.pdf (103.4 kB)
|
.png)
|
| Item type | 報告書 / Research Paper(1) | |||||
|---|---|---|---|---|---|---|
| 公開日 | 2022-11-11 | |||||
| タイトル | ||||||
| タイトル | 微小欠陥を含む部材の応力腐食割れおよび破壊靭性に関する研究 | |||||
| タイトル | ||||||
| タイトル | Stress Corrosion Cracking and Fracture Toughness of Materials with Short Cracks | |||||
| 言語 | en | |||||
| 言語 | ||||||
| 言語 | jpn | |||||
| 資源タイプ | ||||||
| 資源タイプ識別子 | http://purl.org/coar/resource_type/c_18ws | |||||
| 資源タイプ | research report | |||||
| ID登録 | ||||||
| ID登録 | 10.24517/00067922 | |||||
| ID登録タイプ | JaLC | |||||
| 著者 |
広瀬, 幸雄
× 広瀬, 幸雄 |
|||||
| 提供者所属 | ||||||
| 内容記述タイプ | Other | |||||
| 内容記述 | 金沢大学教育学部 | |||||
| 書誌情報 |
昭和62(1987)年度 科学研究費補助金 一般研究(C) 研究成果報告書概要 en : 1987 Fiscal Year Final Research Report Summary 巻 1986 – 1987, p. 2p., 発行日 1989-03-29 |
|||||
| 抄録 | ||||||
| 内容記述タイプ | Abstract | |||||
| 内容記述 | 研究第一年目に製作した交流電位差システムを使用し, 200°C焼戻しされた高張力鋼(SNCM8)切欠き平板(切欠き半径を種々異った場合について)を用い, 空気中および3.5%食塩水中での疲労亀裂伝藩試験を行い, 切欠き底での微小亀裂の開閉口, 伝藩挙動および破面の観察を行った. 更に, 破壊破面および破面下の残留応力をX線回折法で測定し, 疲労試験環境が破面下の残留応力分布に及ぼす影響を検討した. また塑性域深さに関して各種破壊要式の場合と比較した. その主な結果を次にまとめる. (1)切欠き部材での疲労亀裂の伝藩の連統計測に電位差を応用した場合, 光学顕微鏡表面観察では不可能な板厚中央部の非貫通亀裂の成長が測定され, 微小亀裂の初期成長には有効であった. (2)微小疲労亀裂伝藩速度は, 長い亀裂のda/dn-△K関係で予測される早く, かつ△Kのの増大とともに伝藩速度が低下した. これは伝藩速度を有効応力拡大係数範囲△K_<eff>で整理すると, 長い亀裂のdn/dn-△K_<eff>関係に一致した. (3)残留応力が消失する深さωyは最大塑性域深さに対応すると見なされるが, K_<max>との間に次の関係が成立した. ωy=α(K_<max>/σy)^2 ただしσyは降伏応力である. α値は空気中疲労破面で0.19, 食塩水中疲労破面で0.06であった. α値が環境により異なる理由を, 塑性域の降伏応力が異るものとし, その値を評価したが, 食塩水中で著しい材料の硬化が推定される. このα値に関しては, 今後の詳細な研究が必要である. |
|||||
| 抄録 | ||||||
| 内容記述タイプ | Abstract | |||||
| 内容記述 | An AC electrical system with a lock-in amplifier was developed to measure the speciemen of crack in notched specimens of a high strength steel. This system was succesfully used to measure the crack length during SCC and fracture toughnesstests. Crack propagation tests were conducted both in air and in 3.5% NaCl solution. Resisual stress near the fracture surface were measured by X-Ray diffraction method. The results obtained are surmarized as follows; (1) Although the growth rate of short cracks was higher than that predicted from the rate-<DELTA>K relation for long cracks, it was uniquely related to the effective stress intensity factor range and the relation was identical for long cracks. (2) The residual stress measured on the fracture surface was tention both in air-fatigue and corrosion fatigue. The maximum depth of the plastic zone was evaluated on the basis of the residual stress distribution. The depth y is related to K _<max>by the following equation:alpha) ( K_<max>/<delta> y )^2 (omega) y = <alpha> (K_<max>/<delta> y) ^2 where <delta> y is the yield strength obtained in tension tests. <alpha> is 0.19 for air fatigue and 0.06 for corrosion fatigue. The small value of <alpha> in corrosion fatigue suggests the hardening of the material in the plastic zone due to the environmental effect. |
|||||
| 内容記述 | ||||||
| 内容記述タイプ | Other | |||||
| 内容記述 | 研究課題/領域番号:61550052, 研究期間(年度):1986 – 1987 | |||||
| 内容記述 | ||||||
| 内容記述タイプ | Other | |||||
| 内容記述 | 出典：研究課題「微小欠陥を含む部材の応力腐食割れおよび破壊靭性に関する研究」課題番号61550052 （KAKEN：科学研究費助成事業データベース（国立情報学研究所）） （https://kaken.nii.ac.jp/ja/report/KAKENHI-PROJECT-61550052/615500521987kenkyu_seika_hokoku_gaiyo/）を加工して作成 |
|||||
| 著者版フラグ | ||||||
| 出版タイプ | AM | |||||
| 出版タイプResource | http://purl.org/coar/version/c_ab4af688f83e57aa | |||||
| 関連URI | ||||||
| 識別子タイプ | URI | |||||
| 関連識別子 | https://kaken.nii.ac.jp/search/?qm=20019425 | |||||
| 関連名称 | https://kaken.nii.ac.jp/search/?qm=20019425 | |||||
| 関連URI | ||||||
| 識別子タイプ | URI | |||||
| 関連識別子 | https://kaken.nii.ac.jp/ja/grant/KAKENHI-PROJECT-61550052/ | |||||
| 関連名称 | https://kaken.nii.ac.jp/ja/grant/KAKENHI-PROJECT-61550052/ | |||||
| 関連URI | ||||||
| 識別子タイプ | URI | |||||
| 関連識別子 | https://kaken.nii.ac.jp/ja/report/KAKENHI-PROJECT-61550052/615500521987kenkyu_seika_hokoku_gaiyo/ | |||||
| 関連名称 | https://kaken.nii.ac.jp/ja/report/KAKENHI-PROJECT-61550052/615500521987kenkyu_seika_hokoku_gaiyo/ | |||||