{"_buckets": {"deposit": "ef8229c6-b53f-4edf-85b6-84dc5c80978d"}, "_deposit": {"created_by": 18, "id": "60102", "owners": [18], "pid": {"revision_id": 0, "type": "depid", "value": "60102"}, "status": "published"}, "_oai": {"id": "oai:kanazawa-u.repo.nii.ac.jp:00060102", "sets": ["2839"]}, "author_link": ["13046", "2109"], "item_9_biblio_info_8": {"attribute_name": "書誌情報", "attribute_value_mlt": [{"bibliographicIssueDates": {"bibliographicIssueDate": "2016-04-21", "bibliographicIssueDateType": "Issued"}, "bibliographicPageStart": "2p.", "bibliographicVolumeNumber": "1994", "bibliographic_titles": [{"bibliographic_title": "平成6(1994)年度 科学研究費補助金 奨励研究(A) 研究概要"}, {"bibliographic_title": "1994 Research Project Summary", "bibliographic_titleLang": "en"}]}]}, "item_9_creator_33": {"attribute_name": "著者別表示", "attribute_type": "creator", "attribute_value_mlt": [{"creatorNames": [{"creatorName": "Iiyama, Koichi"}], "nameIdentifiers": [{"nameIdentifier": "13046", "nameIdentifierScheme": "WEKO"}, {"nameIdentifier": "90202837", "nameIdentifierScheme": "e-Rad", "nameIdentifierURI": "https://kaken.nii.ac.jp/ja/search/?qm=90202837"}]}]}, "item_9_description_21": {"attribute_name": "抄録", "attribute_value_mlt": [{"subitem_description": "本研究は、希土類元素中の遷移金属であるEr(エルビウム)をドープしたガラスに、光導波路を作製して光導波路形光増幅器を開発するとともに、この光導波路形光増幅器を用いてレーザ発振器を構成することを目的としている。\nまず,光導波路基板として、Erが0.5wt%含まれたクラウンガラスを特注により入手し、その基板表面に、幅7μm、長さ25mmの直線光導波路を作製した。光導波路は、電界イオン交換法によりAg^+イオンを基板表面に拡散させることにより作製した。このように作製した光導波路に励起光(波長1.48μmあるいは波長0.98μm)を入射したところ、1.535μm〜1.542μmの波長において蛍光を観測することができた。そこで、波長1.48μmの励起光を用いて波長1.536μmの信号光の増幅実験を行った。その結果、増幅度は励起光強度が大きいほど、また、信号光強度が小さいほど大きいことがわかり、現在のところ、最大5dBの増幅度を得た。しかしながら、光導波路と光を入出力するための光ファイバとの結合損失が大きく、全体としては正の利得を得ることはできなかった。Erイオンの高濃度化あるいは光導波路の長尺化により、正の利得が得られるものと考えている。また、基板上にリング共振器を構成してレーザ発振を得るための基礎実験として、Erドープ光ファイバを用いた光ファイバリングレーザについて研究を行い、共振器内の光の閉じ込めを強くすることにより、閾値励起光強度は低くなるがスロープ効率は低下することがわかった。また、強度雑音スペクトルにおいて、数10kHzの雑音周波数に緩和振動によるピークが存在することが明らかとなった。", "subitem_description_type": "Abstract"}]}, "item_9_description_22": {"attribute_name": "内容記述", "attribute_value_mlt": [{"subitem_description": "研究課題/領域番号:06750377, 研究期間(年度):1994", "subitem_description_type": "Other"}, {"subitem_description": "出典:研究課題「希土類ドープ光導波路による光増幅素子の作製とその光導波路レーザへの応用」課題番号06750377\n(KAKEN:科学研究費助成事業データベース(国立情報学研究所)) \n(https://kaken.nii.ac.jp/ja/grant/KAKENHI-PROJECT-06750377/)を加工して作成", "subitem_description_type": "Other"}]}, "item_9_description_5": {"attribute_name": "提供者所属", "attribute_value_mlt": [{"subitem_description": "金沢大学自然科学研究科", "subitem_description_type": "Other"}]}, "item_9_identifier_registration": {"attribute_name": "ID登録", "attribute_value_mlt": [{"subitem_identifier_reg_text": "10.24517/00066353", "subitem_identifier_reg_type": "JaLC"}]}, "item_9_relation_28": {"attribute_name": "関連URI", "attribute_value_mlt": [{"subitem_relation_name": [{"subitem_relation_name_text": "https://kaken.nii.ac.jp/ja/search/?kw=90202837"}], "subitem_relation_type_id": {"subitem_relation_type_id_text": "https://kaken.nii.ac.jp/ja/search/?kw=90202837", "subitem_relation_type_select": "URI"}}, {"subitem_relation_name": [{"subitem_relation_name_text": "https://kaken.nii.ac.jp/ja/grant/KAKENHI-PROJECT-06750377/"}], "subitem_relation_type_id": {"subitem_relation_type_id_text": "https://kaken.nii.ac.jp/ja/grant/KAKENHI-PROJECT-06750377/", "subitem_relation_type_select": "URI"}}]}, "item_9_version_type_25": {"attribute_name": "著者版フラグ", "attribute_value_mlt": [{"subitem_version_resource": "http://purl.org/coar/version/c_ab4af688f83e57aa", "subitem_version_type": "AM"}]}, "item_creator": {"attribute_name": "著者", "attribute_type": "creator", "attribute_value_mlt": [{"creatorNames": [{"creatorName": "飯山, 宏一"}], "nameIdentifiers": [{"nameIdentifier": "2109", "nameIdentifierScheme": "WEKO"}, {"nameIdentifier": "90202837", "nameIdentifierScheme": "e-Rad", "nameIdentifierURI": "https://kaken.nii.ac.jp/ja/search/?qm=90202837"}]}]}, "item_files": {"attribute_name": "ファイル情報", "attribute_type": "file", "attribute_value_mlt": [{"accessrole": "open_date", "date": [{"dateType": "Available", "dateValue": "2022-06-27"}], "displaytype": "detail", "download_preview_message": "", "file_order": 0, "filename": "TE-PR-IIYAMA-K-kaken 2016-2p.pdf", "filesize": [{"value": "123.6 kB"}], "format": "application/pdf", "future_date_message": "", "is_thumbnail": false, "licensetype": "license_11", "mimetype": "application/pdf", "size": 123600.0, "url": {"label": "TE-PR-IIYAMA-K-kaken 2016-2p.pdf", "url": "https://kanazawa-u.repo.nii.ac.jp/record/60102/files/TE-PR-IIYAMA-K-kaken 2016-2p.pdf"}, "version_id": "13dd8b3f-4b7d-4b21-b29c-37aaa93db152"}]}, "item_keyword": {"attribute_name": "キーワード", "attribute_value_mlt": [{"subitem_subject": "光通信", "subitem_subject_scheme": "Other"}, {"subitem_subject": "光導波路", "subitem_subject_scheme": "Other"}, {"subitem_subject": "光増幅器", "subitem_subject_scheme": "Other"}]}, "item_language": {"attribute_name": "言語", "attribute_value_mlt": [{"subitem_language": "jpn"}]}, "item_resource_type": {"attribute_name": "資源タイプ", "attribute_value_mlt": [{"resourcetype": "research report", "resourceuri": "http://purl.org/coar/resource_type/c_18ws"}]}, "item_title": "希土類ドープ光導波路による光増幅素子の作製とその光導波路レーザへの応用", "item_titles": {"attribute_name": "タイトル", "attribute_value_mlt": [{"subitem_title": "希土類ドープ光導波路による光増幅素子の作製とその光導波路レーザへの応用"}]}, "item_type_id": "9", "owner": "18", "path": ["2839"], "permalink_uri": "https://doi.org/10.24517/00066353", "pubdate": {"attribute_name": "公開日", "attribute_value": "2022-06-27"}, "publish_date": "2022-06-27", "publish_status": "0", "recid": "60102", "relation": {}, "relation_version_is_last": true, "title": ["希土類ドープ光導波路による光増幅素子の作製とその光導波路レーザへの応用"], "weko_shared_id": -1}
希土類ドープ光導波路による光増幅素子の作製とその光導波路レーザへの応用
https://doi.org/10.24517/00066353
https://doi.org/10.24517/000663530f3895b8-7da6-4eaa-aa09-170f4182c37c
名前 / ファイル | ライセンス | アクション |
---|---|---|
TE-PR-IIYAMA-K-kaken 2016-2p.pdf (123.6 kB)
|
Item type | 報告書 / Research Paper(1) | |||||
---|---|---|---|---|---|---|
公開日 | 2022-06-27 | |||||
タイトル | ||||||
タイトル | 希土類ドープ光導波路による光増幅素子の作製とその光導波路レーザへの応用 | |||||
言語 | ||||||
言語 | jpn | |||||
資源タイプ | ||||||
資源タイプ識別子 | http://purl.org/coar/resource_type/c_18ws | |||||
資源タイプ | research report | |||||
ID登録 | ||||||
ID登録 | 10.24517/00066353 | |||||
ID登録タイプ | JaLC | |||||
著者別表示 |
Iiyama, Koichi
× Iiyama, Koichi |
|||||
提供者所属 | ||||||
内容記述タイプ | Other | |||||
内容記述 | 金沢大学自然科学研究科 | |||||
書誌情報 |
平成6(1994)年度 科学研究費補助金 奨励研究(A) 研究概要 en : 1994 Research Project Summary 巻 1994, p. 2p., 発行日 2016-04-21 |
|||||
抄録 | ||||||
内容記述タイプ | Abstract | |||||
内容記述 | 本研究は、希土類元素中の遷移金属であるEr(エルビウム)をドープしたガラスに、光導波路を作製して光導波路形光増幅器を開発するとともに、この光導波路形光増幅器を用いてレーザ発振器を構成することを目的としている。 まず,光導波路基板として、Erが0.5wt%含まれたクラウンガラスを特注により入手し、その基板表面に、幅7μm、長さ25mmの直線光導波路を作製した。光導波路は、電界イオン交換法によりAg^+イオンを基板表面に拡散させることにより作製した。このように作製した光導波路に励起光(波長1.48μmあるいは波長0.98μm)を入射したところ、1.535μm〜1.542μmの波長において蛍光を観測することができた。そこで、波長1.48μmの励起光を用いて波長1.536μmの信号光の増幅実験を行った。その結果、増幅度は励起光強度が大きいほど、また、信号光強度が小さいほど大きいことがわかり、現在のところ、最大5dBの増幅度を得た。しかしながら、光導波路と光を入出力するための光ファイバとの結合損失が大きく、全体としては正の利得を得ることはできなかった。Erイオンの高濃度化あるいは光導波路の長尺化により、正の利得が得られるものと考えている。また、基板上にリング共振器を構成してレーザ発振を得るための基礎実験として、Erドープ光ファイバを用いた光ファイバリングレーザについて研究を行い、共振器内の光の閉じ込めを強くすることにより、閾値励起光強度は低くなるがスロープ効率は低下することがわかった。また、強度雑音スペクトルにおいて、数10kHzの雑音周波数に緩和振動によるピークが存在することが明らかとなった。 |
|||||
内容記述 | ||||||
内容記述タイプ | Other | |||||
内容記述 | 研究課題/領域番号:06750377, 研究期間(年度):1994 | |||||
内容記述 | ||||||
内容記述タイプ | Other | |||||
内容記述 | 出典:研究課題「希土類ドープ光導波路による光増幅素子の作製とその光導波路レーザへの応用」課題番号06750377 (KAKEN:科学研究費助成事業データベース(国立情報学研究所)) (https://kaken.nii.ac.jp/ja/grant/KAKENHI-PROJECT-06750377/)を加工して作成 |
|||||
著者版フラグ | ||||||
出版タイプ | AM | |||||
出版タイプResource | http://purl.org/coar/version/c_ab4af688f83e57aa | |||||
関連URI | ||||||
識別子タイプ | URI | |||||
関連識別子 | https://kaken.nii.ac.jp/ja/search/?kw=90202837 | |||||
関連名称 | https://kaken.nii.ac.jp/ja/search/?kw=90202837 | |||||
関連URI | ||||||
識別子タイプ | URI | |||||
関連識別子 | https://kaken.nii.ac.jp/ja/grant/KAKENHI-PROJECT-06750377/ | |||||
関連名称 | https://kaken.nii.ac.jp/ja/grant/KAKENHI-PROJECT-06750377/ |