珪酸塩ガラスの静的及び動的圧縮によるナノ構造と物性の変化
https://doi.org/10.24517/00034733
https://doi.org/10.24517/00034733a212affe-2d20-4abf-9f89-e01cf51426db
| 名前 / ファイル | ライセンス | アクション |
|---|---|---|
SC-PR-OKUNO-M-kaken 2007-14p.pdf (742.4 kB)
|
.png)
|
| アイテムタイプ | 報告書 / Research Paper(1) | |||||
|---|---|---|---|---|---|---|
| 公開日 | 2017-10-05 | |||||
| タイトル | ||||||
| タイトル | 珪酸塩ガラスの静的及び動的圧縮によるナノ構造と物性の変化 | |||||
| タイトル | ||||||
| タイトル | Variations of nano-structure and physical properties of silicate glasses by static and shock compressions | |||||
| 言語 | en | |||||
| 言語 | ||||||
| 言語 | jpn | |||||
| 資源タイプ | ||||||
| 資源タイプ識別子 | http://purl.org/coar/resource_type/c_18ws | |||||
| 資源タイプ | research report | |||||
| ID登録 | ||||||
| ID登録 | 10.24517/00034733 | |||||
| ID登録タイプ | JaLC | |||||
| 著者 |
奥野, 正幸
× 奥野, 正幸 |
|||||
| 書誌情報 |
平成18(2006)年度 科学研究費補助金 基盤研究(B) 研究成果報告書 en : 2006 Fiscal Year Final Research Report 巻 2003-2006, p. 14p., 発行日 2007-03-01 |
|||||
| 出版者 | ||||||
| 出版者 | 金沢大学自然科学研究科 | |||||
| 抄録 | ||||||
| 内容記述タイプ | Abstract | |||||
| 内容記述 | 本研究では、珪酸塩ガラスの高圧力下でのナノ構造の変化を明らかにし、地殻下部・マントル上部におけるマグマの挙動及び隕石衝突時の構造変化についての情報を得ることを目的とし、以下のような研究を行った。 1.SiO2ガラスについて静水圧による圧縮実験を行い、15GPaまでの圧縮で約28%の密度増加を確認し、それが、非架橋酸素を持つSiO_4四面体の小さなリング構造(3、4員環)の増加によることを明らかにした、この密度増加は、従来の我々の研究で明らかにした衝撃圧縮での密度増加より大きい。さらに、SiO_2,にGeO_2を加えたガラスについても衝撃圧縮を行い、GeO_2成分の増加に伴い構造変化が起こる圧力が低下することを明らかにした。 2.CaSiO_3-MgSiO_3,組成ガラスの静水圧縮及び衝撃圧縮実験を行い、構造変化をX線回折法、ラマン分光法ならびに分子動力学計算によって調べた。その結果、静水圧での圧縮では7.5GPaで5%前後の密度増加が観測され、X線回折測定、ラマン分光測定ならびに分子動力学計算の結果から、SiO_4四面体の3,4員環の増加が密度増加に寄与していることが明らかとなった。他方、衝撃圧縮では、これらのガラスは殆ど密度増加を示さず、衝撃圧縮ではSiO_4四面体の3,4員環が生成せず圧力の開放とともに構造緩和が起こり密度が変化しなかったと考えられる。 3.オパール試料について、38GPaまでの衝撃実験を行い、そのナノ構造の変化を明らかにした。その結果、オパールは20-30GPaの圧縮で約10%密度が増加し、より高圧では再び密度が減少することを見出した。X線測定の結果から、衝撃圧縮により結晶様の構造が失われ無秩序構造に変化することを明らかにした。 4.上記の研究の多くは、国内学会をはじめ2006年には国際鉱物学連合(IMA)で発表し、学術論文などとして公表した。 | |||||
| 抄録 | ||||||
| 内容記述タイプ | Abstract | |||||
| 内容記述 | In order to obtain information for magma at lower crust and upper mantle regions and structural changes of glass materials by meteorite impacts, the following studies for the nano-structure change of silicate glass under high pressure condition were carried out. 1. SiO_2 glass was compressed under static high pressure up 15 GPa, about 28% of density increase was observed. It was concluded that formations of 3,4 membered rings of SiO_4 tetrahedrons with non bridging oxygen are responsible for the density increase. SiO_2-GeO_2 glasses were also compressed by shock experiments. Increase of GeO_2 component accelerates their structure change. 2. The structures changes of CaSiO_3-MgSiO_3 glasses compressed by static and shock compression were investigated by X-ray diffraction measurements, Raman spectroscopy and Molecular dynamics calculations. About 5% of density increase by static compression of 7.5 GPa was observed. Ii is suggested that this density increase caused by the formations of 3,4 membered rings of SiO_4 tetrahedrons. On the other hand, Almost no density increases were observed for shock compressed CaSiO_3-MgSiO_3 glasses. This fact may indicate that 3,4 membered rings of SiO_4 tetrahedrons may not be formed by shock compression and compressed structure was relaxed by pressure release and subsequent temperature increase. 3. Structural change of opal nano-structure by shock compression was investigated. About 10% of density increase of opal at 20-30 GPa and density decrease at higher pressure. By X-ray diffraction measurements, the crystalline part of opal was change to amorphous state by shock. By IR spectroscopy, OH of opal decrease and frequency of OH band changed toward higher wavenumver were investigated. 4. The results of these studies were presented at National and International Meetings such as IMA and also published as scientific papers. |
|||||
| 内容記述 | ||||||
| 内容記述タイプ | Other | |||||
| 内容記述 | 研究課題/領域番号:15340185, 研究期間(年度):2003–2006 | |||||
| 内容記述 | ||||||
| 内容記述タイプ | Other | |||||
| 内容記述 | 出典：「珪酸塩ガラスの静的及び動的圧縮によるナノ構造と物性の変化」研究成果報告書 課題番号15340185 (KAKEN：科学研究費助成事業データベース（国立情報学研究所）) 本文データは著者版報告書より作成 |
|||||
| 著者版フラグ | ||||||
| 出版タイプ | AM | |||||
| 出版タイプResource | http://purl.org/coar/version/c_ab4af688f83e57aa | |||||
| 関連URI | ||||||
| 識別子タイプ | URI | |||||
| 関連識別子 | https://kaken.nii.ac.jp/search/?qm=40183032 | |||||
| 関連URI | ||||||
| 識別子タイプ | URI | |||||
| 関連識別子 | https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-15340185/ | |||||
| 関連URI | ||||||
| 識別子タイプ | URI | |||||
| 関連識別子 | https://kaken.nii.ac.jp/report/KAKENHI-PROJECT-15340185/153401852006kenkyu_seika_hokoku_gaiyo/ | |||||