高張力4340鋼SCC破面近傍の残留応力分布に及ぼす電極電位の影響(<小特集>X線材料強度小特集)
http://hdl.handle.net/2297/12454
http://hdl.handle.net/2297/124547ef0690f-2622-443b-a22b-870268fa979a
| 名前 / ファイル | ライセンス | アクション |
|---|---|---|
TE-PR-HIROSE-Y-599.pdf (1.9 MB)
|
|
| Item type | 学術雑誌論文 / Journal Article(1) | |||||
|---|---|---|---|---|---|---|
| 公開日 | 2017-10-03 | |||||
| タイトル | ||||||
| タイトル | 高張力4340鋼SCC破面近傍の残留応力分布に及ぼす電極電位の影響(<小特集>X線材料強度小特集) | |||||
| タイトル | ||||||
| タイトル | Residual Stress near SCC Fracture Surface of AISI 4340 Steel under Controlled Electrode Potential(<Minor Special Issue>Minor Special Issue on X-Ray Study on Deformation and Fracture of Solid) | |||||
| 言語 | en | |||||
| 言語 | ||||||
| 言語 | jpn | |||||
| 資源タイプ | ||||||
| 資源タイプ識別子 | http://purl.org/coar/resource_type/c_6501 | |||||
| 資源タイプ | journal article | |||||
| 著者 |
津田, 政明
× 津田, 政明× 広瀬, 幸雄× 矢島, 善次郎× 田中, 啓介 |
|||||
| 提供者所属 | ||||||
| 内容記述タイプ | Other | |||||
| 内容記述 | 金沢大学大学院自然科学研究科 | |||||
| 書誌情報 |
材料=Journal of the Society of Materials Science, Japan 巻 37, 号 417, p. 599-605, 発行日 1988-06-15 |
|||||
| ISSN | ||||||
| 収録物識別子タイプ | ISSN | |||||
| 収録物識別子 | 0514-5163 | |||||
| NCID | ||||||
| 収録物識別子タイプ | NCID | |||||
| 収録物識別子 | AN00096175 | |||||
| 出版者 | ||||||
| 出版者 | 日本材料学会 | |||||
| 抄録 | ||||||
| 内容記述タイプ | Abstract | |||||
| 内容記述 | stress corrosion cracking tests were conducted by using the compact tension (CT) specimens of 200℃ tempered AISI 4340 steel in a 3.5 % NaCl solution environment under various electrode potentials. The distribution of the residual stress beneath the fracture surface was measured with the X-ray electron microscopy. The Effect of electrode potential on the growth kinetics of stress corrosion cracking was discussed on the bases of the results of X-ray observation and scanning microfractography. The results obtained are summarized as follows:(1) The residual stress measured on the fracture surface was tension under cathodic potential. It decreased with increasing potential, and changed to compression under anodic potential. (2) The relation between the plastic zone depth ω_y and the stress intensity factor K can be approximated by the following fracture mechanics equation:ω_y=α(K/σ_Y)^2 were σ_Y is the yield strength. The α value was 0.084 under the free corrosion condition and 0.053 under the catholic polarization condition. | |||||
| 権利 | ||||||
| 権利情報 | 日本材料学会；本文データは日本材料学会の許諾に基づきCiNiiから複製したものである | |||||
| 著者版フラグ | ||||||
| 出版タイプ | VoR | |||||
| 出版タイプResource | http://purl.org/coar/version/c_970fb48d4fbd8a85 | |||||
| 関連URI | ||||||
| 識別子タイプ | URI | |||||
| 関連識別子 | http://ci.nii.ac.jp/naid/110002298734/ | |||||