Mechanical properties of precipitation strengthening Cu-base alloys highly deformed by ARB process
http://hdl.handle.net/2297/29480
http://hdl.handle.net/2297/294803db0d0db-ea7d-499c-ae81-e2d82e2189d6
| 名前 / ファイル | ライセンス | アクション |
|---|---|---|
TE-PR-MONZEN-R-2417.pdf (231.0 kB)
|
|
| Item type | 学術雑誌論文 / Journal Article(1) | |||||
|---|---|---|---|---|---|---|
| 公開日 | 2017-10-03 | |||||
| タイトル | ||||||
| タイトル | Mechanical properties of precipitation strengthening Cu-base alloys highly deformed by ARB process | |||||
| 言語 | ||||||
| 言語 | eng | |||||
| 資源タイプ | ||||||
| 資源タイプ識別子 | http://purl.org/coar/resource_type/c_6501 | |||||
| 資源タイプ | journal article | |||||
| 著者 |
Monzen, Ryoichi
× Monzen, Ryoichi× Takagawa, Yusaku× Watanabe, Chihiro× Terada, Daisuke× Tsuji, N. |
|||||
| 書誌情報 |
Procedia Engineering 巻 10, p. 2417-2422, 発行日 2011-01-01 |
|||||
| ISSN | ||||||
| 収録物識別子タイプ | ISSN | |||||
| 収録物識別子 | 1877-7058 | |||||
| DOI | ||||||
| 関連タイプ | isVersionOf | |||||
| 識別子タイプ | DOI | |||||
| 関連識別子 | 10.1016/j.proeng.2011.04.398 | |||||
| 出版者 | ||||||
| 出版者 | Elsevier | |||||
| 抄録 | ||||||
| 内容記述タイプ | Abstract | |||||
| 内容記述 | The enhancement of strength of Cu-1.2wt%Ni-0.2wt%Be-0.1wt%Zr and Cu-1.4wt%Ni-0.25wt%P-0.1wt%Zr alloys has been tried by the combination of ARB process by 5 cycles and aging treatment at 350 to 450°C. The grain sizes of the alloys, severely deformed by 5-cycle ARB process, were refined down to about 0.4μm. The Cu-Ni-Be-Zr alloy, ARB-processed and peak-aged at 375°C, exhibited a tensile strength σu of 810MPa, an elongation εt of 9% up to failure and an electrical conductivity σ of 62%IACS. The Cu-Ni-P-Zr alloy, initially aged at 450°C, then ARB-processed and peak-aged at 400°C, had the values of σu=780MPa, εt =6% and σ=56%IACS. © 2011 Published by Elsevier Ltd. | |||||
| 著者版フラグ | ||||||
| 出版タイプ | AM | |||||
| 出版タイプResource | http://purl.org/coar/version/c_ab4af688f83e57aa | |||||
| 関連URI | ||||||
| 識別子タイプ | URI | |||||
| 関連識別子 | http://www.elsevier.com/locate/issn/18777058 | |||||