WC-Co超硬合金の疲労き裂進展特性に及ぼす応力比およびWC粒径の影響
http://hdl.handle.net/2297/12321
http://hdl.handle.net/2297/1232180e04c5d-8bba-4b79-9b5f-fd31902016dd
| 名前 / ファイル | ライセンス | アクション |
|---|---|---|
TE-PR-HIROSE-Y-1402.pdf (1.1 MB)
|
|
| Item type | 学術雑誌論文 / Journal Article(1) | |||||
|---|---|---|---|---|---|---|
| 公開日 | 2017-10-03 | |||||
| タイトル | ||||||
| タイトル | WC-Co超硬合金の疲労き裂進展特性に及ぼす応力比およびWC粒径の影響 | |||||
| タイトル | ||||||
| タイトル | Influence of Stress Ratio and WC Grain Size on Fatigue Crack Growth Characteristics of WC-Co Cemented Carbides | |||||
| 言語 | en | |||||
| 言語 | ||||||
| 言語 | jpn | |||||
| 資源タイプ | ||||||
| 資源タイプ識別子 | http://purl.org/coar/resource_type/c_6501 | |||||
| 資源タイプ | journal article | |||||
| 著者 |
広瀬, 幸雄
× 広瀬, 幸雄× 夫, 明煥× 松岡, 秀明× 朴, 栄哲 |
|||||
| 提供者所属 | ||||||
| 内容記述タイプ | Other | |||||
| 内容記述 | 金沢大学大学院自然科学研究科 | |||||
| 書誌情報 |
材料=Journal of the Society of Materials Science, Japan 巻 46, 号 12, p. 1402-1408, 発行日 1997-12-15 |
|||||
| ISSN | ||||||
| 収録物識別子タイプ | ISSN | |||||
| 収録物識別子 | 0514-5163 | |||||
| NCID | ||||||
| 収録物識別子タイプ | NCID | |||||
| 収録物識別子 | AN00096175 | |||||
| 出版者 | ||||||
| 出版者 | 日本材料学会 | |||||
| 抄録 | ||||||
| 内容記述タイプ | Abstract | |||||
| 内容記述 | In order to study the influence of stress ratio and WC grain size, the characteristics of fatigue crack growth were investigated in WC-22wt.%Co cemented carbides with two different grain sizes of 3 and 6μm. Fatigue crack growth tests were carried out over a wide range of fatigue crack growth rate covering the threshold stress intensity factor range ΔK_<th>. The fatigue tests were conducted at 10Hz and two stress ratios R=0.1 and 0.5 in laboratory air at room temperature using the 3-point bending specimens. It was found that the crack growth rate da/dN against the stress intensity factor range ΔK depended on stress ratio R. The crack growth rate plotted in terms of the effective stress intensity factor range ΔK_<eff> (after allowing for crack closure) still exhibited the effect of microstructure. Fractographic examination revealed brittle fracture at R=0.1 and ductile fracture at R=0.5 in Co binder phase. The amount of Co phase transformation was closely related to the fatigue crack growth characteristics. | |||||
| 権利 | ||||||
| 権利情報 | 日本材料学会；本文データは日本材料学会の許諾に基づきCiNiiから複製したものである | |||||
| 著者版フラグ | ||||||
| 出版タイプ | VoR | |||||
| 出版タイプResource | http://purl.org/coar/version/c_970fb48d4fbd8a85 | |||||
| 関連URI | ||||||
| 識別子タイプ | URI | |||||
| 関連識別子 | http://ci.nii.ac.jp/naid/110002293215/ | |||||